Granite
Bala Flower
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
0.44 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.61 |
C-97 |
| MODULUS OF RUPTURE, N / MM2 |
DRY |
23 |
C-99 |
| WET |
22 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
203 |
C-170 |
| WET |
184 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
0.6 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
0.7 |
| FLEXURAL STRENGTH, N/MM2 |
20 |
IS 4860 Guidelines |
Kashmir white
TECHNICAL INFORMATION
(PHYSICO – MECHANICAL PROPERTY) |
VALUE |
ASTM/ INDIAN STANDARDS |
| MINIMUM |
MAXIMUM |
MEAN |
| DENSITY, KG/M3 |
2597 |
2618 |
2608 |
C-97 |
| BULK SPECIFIC GRAVITY |
2.62 |
2.63 |
2.62 |
C-97 |
| ABSORPTION BY WEIGHT % |
0.39 |
0.42 |
0.41 |
C-97 |
| COMPRESSIVE STRENGTH N/ MM2 |
162.17 |
172.61 |
165.98 |
C-170 |
| FLEXURAL STRENGTH, N/MM2 |
8.91 |
9.35 |
9.16 |
C-880 |
| MODULUS OF RUPTURE N/ MM2 |
10.15 |
10.99 |
10.54 |
C-99 |
Merry Gold
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
0.7 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.61 |
C-97 |
| MODULUS OF RUPTURE, N / MM2 |
DRY |
15 |
C-99 |
| WET |
14 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
125 |
C-170 |
| WET |
109 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
0.8 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
1.0 |
| FLEXURAL STRENGTH, N/MM2 |
14 |
IS 4860 Guidelines |
Rosy Pink
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
0.09 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.62 |
C-97 |
| MODULUS OF RUPTURE, N / MM2 |
DRY |
14 |
C-99 |
| WET |
18 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
125 |
C-170 |
| WET |
118 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
0.6 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
0.7 |
| FLEXURAL STRENGTH, N/MM2 |
16 |
IS 4860 Guidelines |
Shivakashi
TECHNICAL INFORMATION
(PHYSICO – MECHANICAL PROPERTY)
|
VALUE |
ASTM/ INDIAN STANDARDS |
| MINIMUM |
MAXIMUM |
MEAN |
| DENSITY, KG/M3 |
2583 |
2597 |
2589 |
C-97 |
| BULK SPECIFIC GRAVITY |
2.60 |
2.61 |
2.60 |
C-97 |
| ABSORPTION BY WEIGHT % |
0.31 |
0.33 |
0.32 |
C-97 |
| COMPRESSIVE STRENGTH N/ MM2 |
148.16 |
158.99 |
154.96 |
C-170 |
| FLEXURAL STRENGTH, N/MM2 |
11.04 |
12.13 |
11.73 |
C-880 |
| MODULUS OF RUPTURE N/ MM2 |
11.79 |
13.29 |
12.37 |
C-99 |
Saphire blue
TECHNICAL INFORMATION
(PHYSICO – MECHANICAL PROPERTY)
|
VALUE |
ASTM/ INDIAN STANDARDS |
| MINIMUM |
MAXIMUM |
MEAN |
| DENSITY, KG/M3 |
2686 |
2702 |
2697 |
C-97 |
| BULK SPECIFIC GRAVITY |
2.70 |
2.71 |
2.71 |
C-97 |
| ABSORPTION BY WEIGHT % |
0.13 |
0.13 |
0.13 |
C-97 |
| COMPRESSIVE STRENGTH N/ MM2 |
137.89 |
148.95 |
143.15 |
C-170 |
| FLEXURAL STRENGTH, N/MM2 |
9.17 |
11.97 |
10.72 |
C-880 |
| MODULUS OF RUPTURE N/ MM2 |
12.90 |
14.10 |
13.62 |
C-99 |
Tan Brown
TECHNICAL INFORMATION
(PHYSICO – MECHANICAL PROPERTY)
|
VALUE |
ASTM/ INDIAN STANDARDS |
| MINIMUM |
MAXIMUM |
MEAN |
| DENSITY, KG/M3 |
2698 |
2713 |
2706 |
C-97 |
| BULK SPECIFIC GRAVITY |
2.71 |
2.72 |
2.72 |
C-97 |
| ABSORPTION BY WEIGHT % |
0.11 |
0.12 |
0.11 |
C-97 |
| COMPRESSIVE STRENGTH N/ MM2 |
179.69 |
184.41 |
181.83 |
C-170 |
| FLEXURAL STRENGTH, N/MM2 |
6.21 |
8.71 |
7.34 |
C-880 |
| MODULUS OF RUPTURE N/ MM2 |
8.88 |
11.28 |
10.34 |
C-99 |
Lavender
TECHNICAL INFORMATION
(PHYSICO – MECHANICAL PROPERTY)
|
VALUE |
ASTM/ INDIAN STANDARDS |
| MINIMUM |
MAXIMUM |
MEAN |
| DENSITY, KG/M3 |
2672 |
2699 |
2683 |
C-97 |
| BULK SPECIFIC GRAVITY |
2.69 |
2.70 |
2.69 |
C-97 |
| ABSORPTION BY WEIGHT % |
0.22 |
0.23 |
0.23 |
C-97 |
| COMPRESSIVE STRENGTH N/ MM2 |
188.09 |
205.04 |
196.06 |
C-170 |
| FLEXURAL STRENGTH, N/MM2 |
14.64 |
15.82 |
15.14 |
C-880 |
| MODULUS OF RUPTURE N/ MM2 |
12.37 |
14.85 |
13.67 |
C-99 |
|
Limestone
Midnight Black
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.23 |
BS 680 PT2 |
| WETTING & DRYING TEST |
NO SIGNS OF DELAMINATION/SPLITTING ALONG THE EDGES WHEN EXAMINED THROUGH A LENS, NOR OF FLAKING OF THE SURFACE |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
NO SIGNS OF DELAMINATION ALONG THE EDGES WHEN EXAMINED THROUGH A LENS, NOR OF SWELLING OR SOFTENING OR FLAKING OF THE SURFACE AND NO GASEOUS EVOLUTION DURING IMMERSION |
BS 680 PT2 |
Ocean Blue
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
0.26 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.67 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
39 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
30 |
C-99 |
| WET |
PARALLEL TO RIFT |
28 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
32 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
172 |
C-170 |
| PERPENDICULAR TO RIFT |
92 |
| WET |
PARALLEL TO RIFT |
126 |
| PERPENDICULAR TO RIFT |
70 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
2.2 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
2.5 |
Sandy Straw
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
0.23 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.69 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
44 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
40 |
C-99 |
| WET |
PARALLEL TO RIFT |
37 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
33 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
88 |
C-170 |
| PERPENDICULAR TO RIFT |
96 |
| WET |
PARALLEL TO RIFT |
79 |
| PERPENDICULAR TO RIFT |
86 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
3.3 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
3.5 |
|
Marble
Black Elegance
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
0.03 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.72 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
22 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
19 |
C-99 |
| WET |
PARALLEL TO RIFT |
18 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
21 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
73 |
C-170 |
| PERPENDICULAR TO RIFT |
70 |
| WET |
PARALLEL TO RIFT |
72 |
| PERPENDICULAR TO RIFT |
57 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
4.1 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
4.3 |
| Flexural strength, N/mm2 |
21 |
IS 4860 Guidelines |
Rainforest Brown
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
2.38 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.55 |
C-97 |
| MODULUS OF RUPTURE, N / MM2 |
DRY |
19 |
C-99 |
| WET |
13 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
138 |
C-170 |
| WET |
83 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
1.4 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
1.6 |
| FLEXURAL STRENGTH, N/MM2 |
12 |
IS 4860 Guidelines |
Rainforest Green
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
2.38 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.55 |
C-97 |
| MODULUS OF RUPTURE, N / MM2 |
DRY |
19 |
C-99 |
| WET |
13 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
138 |
C-170 |
| WET |
83 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
1.4 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
1.6 |
| FLEXURAL STRENGTH, N/MM2 |
12 |
IS 4860 Guidelines |
Golden Brown
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
2.38 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.55 |
C-97 |
| MODULUS OF RUPTURE, N / MM2 |
DRY |
19 |
C-99 |
| WET |
13 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
138 |
C-170 |
| WET |
83 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
1.4 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
1.6 |
| FLEXURAL STRENGTH, N/MM2 |
12 |
IS 4860 Guidelines |
|
Sandstone
Misty Grove
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.84 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Soft Mocha
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.84 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Hazelnut
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.84 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Desert Indigo
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.84 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Golden Oak
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.84 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Oyester Grey
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.84 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Peanut Grey
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
0.84 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Ochre Yellow
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
3.00 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Shrubby Mint
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
3.00 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
Spicy Caramel
| TECHNICAL INFORMATION |
VALUE/ RESULT |
TEST METHOD
(BRITISH STANDARD)
|
| WATER ABSORPTION, WEIGHT % |
3.00 |
BS 680 PT2 |
| WETTING & DRYING TEST |
No signs of delamination/splitting along the edges when examined through a lens, nor of flaking of the surface |
BS 680 PT2 |
| SULPHURIC ACID IMMERSION TEST |
No signs of delamination along the edges when examined through a lens, nor of swelling or softening or flaking of the surface and no gaseous evolution during immersion |
BS 680 PT2 |
MeriGold Yellow
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
1.91 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.44 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
19 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
19 |
C-99 |
| WET |
PARALLEL TO RIFT |
13 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
18 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
138 |
C-170 |
| PERPENDICULAR TO RIFT |
117 |
| WET |
PARALLEL TO RIFT |
104 |
| PERPENDICULAR TO RIFT |
62 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
2.8 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
3.0 |
Dusty Beije
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
1.91 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.44 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
19 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
19 |
C-99 |
| WET |
PARALLEL TO RIFT |
13 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
18 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
138 |
C-170 |
| PERPENDICULAR TO RIFT |
117 |
| WET |
PARALLEL TO RIFT |
104 |
| PERPENDICULAR TO RIFT |
62 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
2.8 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
3.0 |
Ivory Fantasy
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
1.82 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.36 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
16 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
9 |
C-99 |
| WET |
PARALLEL TO RIFT |
13 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
8 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
115 |
C-170 |
| PERPENDICULAR TO RIFT |
108 |
| WET |
PARALLEL TO RIFT |
105 |
| PERPENDICULAR TO RIFT |
91 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
2.9 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
3.1 |
Seashell Rose
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
0.53 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.60 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
42 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
40 |
C-99 |
| WET |
PARALLEL TO RIFT |
34 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
39 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
156 |
C-170 |
| PERPENDICULAR TO RIFT |
185 |
| WET |
PARALLEL TO RIFT |
134 |
| PERPENDICULAR TO RIFT |
153 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
0.9 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
1.0 |
Rainbow
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
5.0 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.11 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
11 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
9 |
C-99 |
| WET |
PARALLEL TO RIFT |
10 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
7 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
63 |
C-170 |
| PERPENDICULAR TO RIFT |
61 |
| WET |
PARALLEL TO RIFT |
27 |
| PERPENDICULAR TO RIFT |
20 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
5.2 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
5.4 |
Teak
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN STANDARDS |
| WATER ABSORPTION, % BY WEIGHT |
6.29 |
C-97 |
| DENSITY (BULK SPECIFIC GRAVITY) |
2.07 |
C-97 |
| MODULUS OF RUPTURE, N/ MM2 |
DRY |
PARALLEL TO RIFT |
8 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
9 |
C-99 |
| WET |
PARALLEL TO RIFT |
8 |
C-99 GUIDELINES |
| PERPENDICULAR TO RIFT |
6 |
C-99 |
| COMPRESSIVE STRENGTH N/ MM2 |
DRY |
PARALLEL TO RIFT |
41 |
C-170 |
| PERPENDICULAR TO RIFT |
49 |
| WET |
PARALLEL TO RIFT |
31 |
| PERPENDICULAR TO RIFT |
36 |
| ABRASION (RESISTANCE TO WEAR) |
Average wear, mm |
5.2 |
IS 1237 Guidelines |
| MAX. WEAR ON INDIVIDUAL SPECIMEN, MM |
5.3 |
|
SlateStone
Copper
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN Standards
|
| Modulus of rupture, N/ mm2 |
14 |
C-120 |
| Water absorption, % by weight |
1.2 |
C-121 |
| Acid Resistance (Whether Resistance), Depth of softening mm |
0.09 |
C-217 |
| Abrasion (Resistance to wear) |
Average wear, mm |
11.7 |
IS 1237 Guidelines |
| Max. wear on individual Specimen, mm |
11.7 |
deoli green
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN Standards
|
| Modulus of rupture, N/ mm2 |
19 |
C-120 |
| Water absorption, % by weight |
2.4 |
C-121 |
| Acid Resistance (Whether Resistance), Depth of softening mm |
0.05 |
C-217 |
| Abrasion (Resistance to wear) |
Average wear, mm |
5.7 |
IS 1237 Guidelines |
| Max. wear on individual Specimen, mm |
5.9 |
Himachal Black
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN Standards
|
| Modulus of rupture, N/ mm2 |
41 |
C-120 |
| Water absorption, % by weight |
0.7 |
C-121 |
| Acid Resistance (Whether Resistance), Depth of softening mm |
0.05 |
C-217 |
| Abrasion (Resistance to wear) |
Average wear, mm |
3.0 |
IS 1237 Guidelines |
| Max. wear on individual Specimen, mm |
3.2 |
Peacock
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN Standards
|
| Modulus of rupture, N/ mm2 |
27 |
C-120 |
| Water absorption, % by weight |
3.1 |
C-121 |
| Acid Resistance (Whether Resistance), Depth of softening mm |
0.08 |
C-217 |
| Abrasion (Resistance to wear) |
Average wear, mm |
10.3 |
IS 1237 Guidelines |
| Max. wear on individual Specimen, mm |
10.5 |
Silver Grey
| TECHNICAL INFORMATION |
VALUE |
ASTM/ INDIAN Standards
|
| Modulus of rupture, N/ mm2 |
46 |
C-120 |
| Water absorption, % by weight |
0.3 |
C-121 |
| Acid Resistance (Whether Resistance), Depth of softening mm |
0.05 |
C-217 |
| Abrasion (Resistance to wear) |
Average wear, mm |
2.6 |
IS 1237 Guidelines |
| Max. wear on individual Specimen, mm |
2.8 |
|